| Taille du grain | |
|---|---|
| < 0.2 μm | nano |
| 0.2 - 0.5 μm | ultra fin |
| 0.5 - 0.8 μm | sub-micro |
| 0.8 - 1.3 μm | fin |
| 1.3 - 2.5 μm | moyen |
| 2.5 - 6.0 μm | gros |
| > 6.0 μm | extra-gros |
| Description / Nuance | Qualité ISO ISO 513 |
Liant Cobalt % |
Autres % |
Taille du grain ISO 4499-2 |
Densité g/cm3 |
Dureté | Résistance à la rupture transversale N/mm2 |
Force de compression N/mm2 |
|
|---|---|---|---|---|---|---|---|---|---|
| HV 30 ISO 3878 |
HRA ISO 3738-1 |
||||||||
| SCS 06 | K05 - K10 | 6 | 0.20 | sub-micro | 14.95 | 1770 | 93.1 | 2500 | 7250 |
| SCS 08 | K10 - K30 | 8 | 0.35 | sub-micro | 14.75 | 1685 | 92.6 | 2850 | 7000 |
| SCS 10 | K20 - K40 | 10 | 0.50 | sub-micro | 14.48 | 1600 | 92.1 | 3250 | 6600 |
| SCM 12 | K40 | 12 | 0.50 | moyen | 14.25 | 1295 | 89.6 | 3100 | 5800 |
| SCM 15 | > K40 | 15 | 0.50 | moyen | 13.96 | 1210 | 88.7 | 3250 | 5500 |
| SCG 15 | - | 15 | - | gros | 14.00 | 1030 | 86.5 | 2900 | 4600 |
| SCG 20 | - | 20 | - | gros | 13.55 | 910 | 85.0 | 2900 | 4150 |
| Description / Nuance | Qualité ISO ISO 513 |
Liant Nickel % |
Autres % |
Taille du grain ISO 4499-2 |
Densité g/cm3 |
Dureté | Résistance à la rupture transversale N/mm2 |
Force de compression N/mm2 |
|
|---|---|---|---|---|---|---|---|---|---|
| HV 30 ISO 3878 |
HRA ISO 3738-1 |
||||||||
| SCF 06 N | - | 6 | 0.10 | fin | 14.95 | 1500 | 91.3 | 2200 | 4500 |
| SCF 10 N | - | 10 | 0.50 | fin | 14.41 | 1350 | 90.1 | 2600 | 3900 |